- Highly precise resin for investment molding
-
Burns out with no residue
-
Compatible with rapid burnout and gradual temperature ramp workflows, with no residual ash - Used with chrome, cobalt, gold, and silver
- Low shrinkage formula controls thermal expansion to yield pore-free and accurate castings
|
PROPERTY |
PROCEDURE ASTM D790 |
KEYCAST 15 |
| Flexural Modulus (MPa) | ASTM D790 | 340 |
| Tensile Strength | ASTM D638 | 9.1 |
| Young's Modulus (MPa) | ASTM D638 | 220 |
| Elongation at Break % | ASTM D638 | 16% |
| CTE 0-150˚C (32-302˚F) | ASTM E831 | 168 x 10-6m/(m.˚C) |
| CTE 150-250˚C (302-482˚F) | ASTM E831 | 64 x 10-6m/(m.˚C) |
| CTE >250˚C (>482˚F) | ASTM E831 | <0m/(m.˚C) |
| Shrinkage | ASTM D792 | <2% |